ONE.MIM sintering
Hlau txhaj tshuaj molding txheej txheem Feem ntau suav nrog cov khoom tsim, pwm tsim, kev ntsuas zoo, sib tov, molding, degreasing, sintering, theem nrab ua thiab lwm yam 8 qhov tseem ceeb txuas, JH MIM tuaj yeem hloov kho degreasing thiab sintering khoom raws li cov neeg siv khoom thiab cov txheej txheem yuav tsum tau ua, thiab tuaj yeem ua ke ua ke rau muab lub tshuab nqus tsev degreasing thiab sintering integrated khoom.
1, graphite thermal teb lub tshuab nqus tsev degreasing sintering integrated khoom;
Khoom siv tsim nyog:
Hlau nickel alloy, feem ntau stainless hlau (17-4ph, 316L, PANACEA, thiab lwm yam), tuag steel, siab ceev hlau, thiab lwm yam
Jiehuang MIM muaj cov kev daws teeb meem hauv qab no rau cov hlau-nickel alloys, stainless hlau (17-4ph, 316L, PANACEA, thiab lwm yam), tuag steel, siab ceev steel, thiab lwm yam.:
ID | HWV 4415 |
Qauv nab npawb | VHSgr-40/40/150-1600 |
Lub sijhawm ua haujlwm zoo (mm) | 400 × 400 × 1500 hli |
Nqa hnyav | 300 KG |
Lub zog cua sov / tag nrho lub zog | 240KW/280KW TSI |
Tsim kub | 1600 ℃ |
Ua haujlwm kub | 1550 ℃ |
Kub tswj hom | Ob qhov ntsuas kub |
Kub kub uniformity | ≤ ± 3 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; 10 ℃ / min (1000-1550 ℃) |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤ 30 ℃, cua sov siab 9bar) | 1450 txog 100 degrees, 5 mus rau 7 teev |
2, hlau kub teb lub tshuab nqus tsev degreasing sintering integrated khoom;
Cov khoom tsim nyog
Tsawg-carbon stainless hlau, titanium alloy (Ti, TC4), tooj liab alloy, tungsten alloy, superalloy (718, 713), thiab lwm yam
Jiehuang MIM yog ib tug series ntawm cov ntaub ntawv: low-carbon stainless hlau, titanium alloy (Ti, TC4), tooj liab alloy, tungsten alloy, superalloy (718, 713), thiab lwm yam. Peb muab cov nram qab no kev daws teeb meem:
Qauv nab npawb | VHS4412-M |
Qauv nab npawb | VHSmo-42/45/125-1600 |
Lub sijhawm ua haujlwm zoo (mm) | 420 × 450 × 1250 hli |
Nqa hnyav | 300 KG |
Lub zog cua sov / tag nrho lub zog | 240KW/280KW TSI |
Tsim kub | 1600 ℃ |
Ua haujlwm kub | 1550 ℃ |
Kub tswj hom | Ob qhov ntsuas kub |
Kub kub uniformity | ≤ ± 3 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤30 ℃, qhov cub siab 9bar) | 1450 txog 100 degrees, 8 mus rau 10 teev |
OB, MIM siab degreasing sintering
Txheej txheem khiav thiab kev taw qhia
Lub hom phiaj ntawm qhov tsis zoo ntawm lub tshuab nqus tsev sintering txheej txheem cov khoom lag luam, lub siab degreasing sintering integrated rauv tau tsim, uas tuaj yeem ua rau kom cov sintering ntom ntom ntawm cov khoom ntawm qhov kub thiab txias los ntawm kev kub siab.
1, 1MPa graphite thermal teb lub tshuab nqus tsev siab degreasing sintering integrated khoom;
Khoom siv tsim nyog:
Tungsten carbide, titanium carbide, tantalum carbide, thiab lwm yam.
Jiehuang MIM1MPa siab degreasing sintering specifications:
ID | PHS4412-1 |
Qauv nab npawb | PHSgr-40/40/120-1600 |
Lub sijhawm ua haujlwm zoo (mm) | 400 × 400 × 1200 (mm) |
Nqa hnyav | 600 KG |
Lub zog cua sov / tag nrho lub zog | 240KW/280KW TSI |
Tsim siab | 1 MPa |
Ua hauj lwm siab | 0.96MPa ua |
Tsim kub | 1600 ℃ |
Ua haujlwm kub | 1550 ℃ |
Kub tswj hom | Peb txoj siv kub tswj |
Kub kub uniformity | ≤ ± 5 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤30 ℃, qhov cub siab 9bar) | 1450 txog 100 degrees, rau rau yim teev |
2, 6MPa graphite thermal teb lub tshuab nqus tsev siab degreasing sintering integrated khoom;
Cov khoom tsim nyog
Tungsten carbide, titanium carbide, tantalum carbide, thiab lwm yam.
Jiehuang MIM 6MPa siab degreasing sintering specifications:
ID | PHS4412-6 |
Qauv nab npawb | PHSgr-40/40/120-1600 |
Lub sijhawm ua haujlwm zoo (mm) | 400 × 400 × 1200 (mm) |
Lub nra hnyav | 600 KG |
Lub zog cua sov / tag nrho lub zog | 300KW/340KW TSI |
Tsim siab | 6 MPa ua |
Ua hauj lwm siab | 5,80MPa |
Tsim kub | 1600 ℃ |
Ua haujlwm kub | 1550 ℃ |
Kub tswj hom | Peb txoj siv kub tswj |
Kub kub uniformity | ≤ ± 5 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤30 ℃, qhov cub siab 50bar) | 1450 txog 100 degrees, 6 mus rau 8 teev |
3, 10MPa graphite thermal teb lub tshuab nqus tsev siab degreasing sintering integrated khoom;
Cov khoom tsim nyog
Tungsten carbide, titanium carbide, tantalum carbide, thiab lwm yam.
Jiehuang MIM 10MPa siab degreasing sintering specifications:
ID | PHS 4412-10 |
Qauv nab npawb | PHSgr-40/40/120-1600 |
Lub sijhawm ua haujlwm zoo (mm) | 400 × 400 × 1200 (mm) |
Lub nra hnyav | 600 KG |
Lub zog cua sov / tag nrho lub zog | 370KW/410KW TSI |
Tsim siab | 10 MPa |
Ua hauj lwm siab | 9.50MPa ua |
Tsim kub | 1600 ℃ |
Ua haujlwm kub | 1550 ℃ |
Kub tswj hom | Peb txoj siv kub tswj |
Kub kub uniformity | ≤ ± 5 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤30 ℃, qhov cub siab 50bar) | 1450 txog 100 degrees, 5 mus rau 7 teev |
Peb, CIM atmospheric siab sintering
Graphite thermal teb lub tshuab nqus tsev degreasing sintering integrated khoom;
Ceramic txhaj tshuaj molding txheej txheemFeem ntau suav nrog cov khoom tsim, pwm tsim, kev ntsuas zoo, sib tov, sib sau, degreasing, sintering, theem nrab ua thiab lwm yam 8 qhov tseem ceeb txuas, Jiehuang MIMtuaj yeem kho cov khoom siv degreasing thiab sintering raws li cov neeg siv khoom cov khoom thiab cov txheej txheem, thiab tuaj yeem ua ke ua ke los muab cov khoom siv nqus degreasing thiab sintering integrated khoom.
Cov khoom tsim nyog
Zirconia, alumina, silicon nitride, silicon carbide, thiab lwm yam.;
Jiehuang CIM tov yog raws li nram no:
Lub ntsiab nta yog raws li nram no:
- Cov khoom uas muaj cov duab geometric complex tuaj yeem npaj tau dawb thiab ncaj qha.
- Lub voj voog tsim yog luv, tsuas yog kaum ntawm ib-pua pua ntawm lub sij hawm pouring thiab kub nias molding, lub zog ntawm lub billet yog siab, ntau lawm yuav automated, thiab kev tswj thiab tswj cov txheej txheem ntau lawm kuj yooj yim, haum rau ntau lawm.
- Vim qhov zoo fluidity ntawm lub binder, qhov ceev ntawm txhaj molding billet yog heev uniform.
- Vim tias qhov sib ntxiv ntawm ntau cov binders hauv kev txhaj tshuaj molding, lub sij hawm degreasing yog ntev, tshwj xeeb tshaj yog rau cov khoom uas muaj tuab tuab, lub sij hawm degreasing yuav ntev li 100-200 teev.
- Vim tias cov hmoov thiab cov khoom sib tov sib xyaw zoo sib xws, qhov sib txawv ntawm cov hmoov yog me me, thiab cov yam ntxwv ntawm lub shrinkage nyob rau hauv cov txheej txheem sintering yog qhov zoo ib yam, yog li cov khoom muaj qhov sib txawv ntom ntom hauv txhua qhov chaw thiab siab geometric raug.
- Siv tau qhov loj me: 400X400X1500mm
- Kev ntsuas kub tsis sib xws: ± 3 ℃
ID | HWV 4415 |
Qauv nab npawb | VHSgr-40/40/150-1800 |
Lub sijhawm ua haujlwm zoo (mm) | 450 × 450 × 1500 (mm) |
Nqa hnyav | 300 KG |
Lub zog cua sov / tag nrho lub zog | 240KW/280KW TSI |
Tsim kub | 1800 ℃ |
Ua haujlwm kub | 1750 ℃ |
Kub tswj hom | 2 aav |
Kub kub uniformity | ≤ ± 3 ℃ |
Cua sov tus nqi | 15 ℃ / min (≤ 1000 ℃) ; 10 ℃ / min (1000-1550 ℃) |
Limiting lub tshuab nqus tsev | Txias, npliag, huv rauv, ≤ 2Pa |
Lub tshuab nqus tsev vacuum | Txias, npliag, huv rauv, ≤ 2Pa / h |
Wax tawm los | ≥98﹪ |
Txias tus nqi (tag nrho rauv)
(Cov dej txias hauv qhov ntsuas kub ≤ 30 ℃, cua sov siab 9bar) | 1450 txog 100 degrees, 5 mus rau 7 teev |
Post lub sij hawm: Dec-06-2023