Applicatur materiae forMetallum iniectio corona:
MIM processus applicatur ad amplis materiis, incluso ferro admixto, ferro immaculato, ferro ferramento, nickel ima mixtura, stannum stannum, stannum durum, titanium stannum, materiae magneticae, Kovar stannum, ceramicum denique, etc.
Quales metalla producta sunt idoneaeMIM processus:
1. Pondus MIM components plerumque est 0.2g - 200g.
2. Area projecta est 100 centimetra quadrata.
3. MIM partium magnitudo accurate supra 10MM est ±0,5%.
4. Partes MIM maximae crassitudinis muri est 10MM.
5. Minimum magnitudine 0.2MM.
Mensa 1 Communiter MIM materiae adsueta eorumque applicatione agrorum;
| Materia systema | Admisce notam, compositionem | Applicationem agri |
| Humilis stannum chalybe | Fe-2Ni、Fe-8Ni | Varii partes structurae autocineti, machinae et aliae industriae |
| Diver | 316L 、 17-4PH、 420、 440C Tabula II Proprietates materiae communium MIM: | Instrumenta medica, partes vigiliae |
| durum mixtura | WC-Quid? | Omnia cultri, horologiorum, vigiliarum |
| tellus | Al2O3, ZrO2, SiO2 | IT electronicas, necessitates quotidianas, horologia et vigilias |
| Gravis alloy | W-Ni-Fe、W-Ni-Cu、W-Cu | Industria militaris, communicationes, necessaria quotidiana |
| Titanium alloy | Ti、Ti-6Al-4V | Medicorum et militarium partium structurarum |
| Materia magnetica | Fe、 NdFeB SmCo5、Fe-Si | Variae partes magneticae |
| instrumentum chalybe | CrMo4, M2 | Varius instrumenta |
Tabula II Proprietates materiae communium MIM:
| Designatio materialis | Admisce Compositio (wt%) |
Conditio | Density p (g/cm³) | UTS σ b(Mpa) | YS' σ 0.2(Mpa) | Prolongatio σ (%) |
duritia |
| Humilis Alloy Ferro | |||||||
| MIM4600 (MIM2200) | Ad 1.5~2.5% Mo 0.5% max Fe balance |
Sinterd |
7.50 |
290 |
125 |
40 |
45~65HRB |
| MIM4600 (modeifed) (MIM2700) | Ad 6.5~8.5% Mo 0.5% max Fe balance |
Sinterd |
7.60 |
410 |
210 |
26 |
70~90HRB |
|
MIM4605 | Ni 1.5~2.5% Mo 0.2~0.5% C 0.4~0.6% Fe- bilance |
Sinterd |
7.50 |
415 |
255 |
15 |
65-85HRB |
| Caloris agitur | 7.50 | 1655 | 1480 | 2 | 45~50HRC | ||
|
MIM4140 | Ad 0.75~1.25% Cr 0.75~1.25% Mo 0.75% max C 0.3~0.5% Fe- bilance |
Sinterd |
7.50 |
820 |
620 |
10 |
70~100HRB |
|
Caloris agitur |
7.50 |
1400 |
820 |
5 |
45~45HRC | ||
| Diver | |||||||
|
MIM SS316L | C 0.03%max Ni 10~14% Mo 2~3% Cr 18~20% Fe- bilance |
Sinterd |
7.75 |
500 |
250 |
4 |
65~85HRB |
|
MIM SS304 | C 0.08% max Ni 8~10% Cr 18~20% Fe- bilance |
Sinterd |
7.65 |
480 |
270 |
35 |
65~85HRB |
|
MIM SS420 | C 0.2~0.4% Cr 12~14% Fe- bilance | Caloris agitur |
7.40 |
1310 |
11500 |
6 |
40~45HRC |
|
MIM 17-4PH | C 0.07%max Cr 15.5~17.5% Cu 3~5% Ni 3~5% Nb 0.15~0.45% Fe- bilance |
Sinterd |
7.50 |
900 |
730 |
6 |
20~28HRC |
|
Caloris agitur |
7.50 |
1185 |
1090 |
5 |
32~ 42HRC | ||
| MIM SS310S |
| Sinterd | 7.70 | 520 | 205 | 40 | 80~100HRB |
| Magnetica Materia | |||||||
|
MIM Fe3Si | C0.05% Ita 2.5~ 3.5% Fe- bilance |
Sinterd |
7.60 |
530 |
390 |
24 |
75~85HRB |
|
MIM Fe50Ni | C 0.05%max Ni 49~51% Fe- bilance |
Sinterd |
7.70 |
455 |
160 |
30 |
50~65HRB |
|
MIM Fe50Co | C 0.05% max Co 48~50% Fe- bilance |
Sinterd |
7.70 |
205 |
140 |
~1.0 |
65~85HRB |
|
MIM SS430 | C 0.05max Cr 16~18% Fe- bilance |
Sinterd |
7.50 |
400 |
240 |
25 |
65~ HRB |
|
|
|
|
|
|
|
|
|
Tabula 3 comparatio inter MIM et alios processuum;
| Comparatio project | ME | P/M | Die Casting | Investment Iactare | Machining |
| Pars densitas | Summus | low | Summus | Fair | Summus |
| Pars distrahens vi | 0.5mm | 1mm | 0.8mm | 2mm | 0.5mm |
| Pars superficies metam | μ m Ra | Coares | Medium | Medium 5 μm Ra | Fine |
| partes miniaturization facultatem |
bonum |
Fair |
Pauper |
Fair |
bonum |
| Partes tenues facultatem |
Multi |
Mediocris |
pauci |
Mediocris |
Multi |
| Partes multiplicitate | 95~100% |
| 99~100% | 99~100% | 99~100% |
| Tolerantia part design | Mediocris | Summus | Mediocris | Mediocris | Summus |
| Massa productio facultatem |
bonum |
Pauper |
Fair |
bonum |
bonum |
| Acta materia range | Summus | Summus | Summus | Fair | low |
| Facultatem copiam | Mediocris | low | low | Mediocris | Summus |
Metallum iniectio nova estpulveris metallurgy processus, potest producere partes densitatis et complexae figurae sine machinis. Cum notis singularibus materiae MIM, MIM praecisionem facere potest partes metallicae pro variis fructibus, inclusis autocinetis, telephoniis gestabilibus, instrumentis manibus, instrumentis dentalibus, instrumentis pneumaticis, instrumentis chirurgicis manu, instrumentis chirurgicis, bonis lusis et computatoribus laptop. Plerumque usus materiae metallicae in MIM processu sunt immaculati ferrum, mixtura ferri et mollis materia magnetica.